Zirconia 3Y 3D Printing Paste
OXIDE CERAMICS
ZrO2, material with the very good mechanical properties cold, being able to be colored for applications in jewelry, excellent mechanical properties in the high temperatures, the weak thermal conductivity at room temperature, conductor in T> 1000°C, great hardness, good wear resistance, good chemical slowness, good resistance in the attacks of metals.
-
Compatible platform:
CERAMIC SLA
-
Type:
Ceramic Pastes
Request a quote
-
Categories:
Materials, Ceramic, Composite Tooling, Dental, Engineering, Jigs&Fixtures, Manufacturing, Medical, Paste, SLA Ceramic, Slurry
- Description
- Details
- Materials
- Documents
- Videos
- Review
Description
Properties
- Excellent mechanical properties
- Chemical inertness
- High Hardness
Applications
- Jewerly
- Watches
- Biomédical devices
- Biomedical implants
- Electronic equipment
PHYSICAL AND MECHANICAL PROPERTIES
| Densification rate | > 99.5% | |
| Density | > 5.95 g/cm3 | |
| Grain size after sintering | < 0.5 μm | |
| 4-pt bending strength | 950 MPa | |
| Weibukk modules | 9 | |
| Theorical Young modulus | 200 GPa | |
| Vickers hardness | 12.6 GPa | |
| Shear modulus | 79.8 GPa | |
| Compressive strength | 2070 MPa | |
| Thermal properties from -50°C to 60 °C | ||
| Thermal conductivity at RT | 3.3 W/m.K | |
| Thermal expansion coefficient | at -50 °C | 8.59 *10^-6 K^-1 |
| at 20 °C | 9.10 *10^-6 K^-1 | |
| at 60°C | 9.34 *10^-6 K^-1 | |
- Brand 3DCeram
- Weight 5 kg
- Country of origin France
- Printing Materials Ceramic Pastes
- Technology CERAMIC SLA